ADVANTAGES
• Very good chemical resistanc
• Excellent adhesion to cold, damp
• Improved film appearance
• Long pot life
• Good strength and modulus
APPLICATIONS
• Concrete primers, adhesives and bonding agents
• Self-leveling and trowelable flooring
• Tile grouts
• Chemically-resistant mortars and grouts
STORAGE LIFE
At least 24 months from the date of manufacture in the original sealed container at ambient temperature. Store away from excessive heat and humidity in tightly closed containers.
HANDLING PRECAUTIONS
Refer to the Material Safety Data Sheet for Ancamide 2396 curing agent.
TYPICAL CURE SCHEDULE
7 days at ambient temperature.
TYPICAL PROPERTIES | |
| Appearance | Amber liquid |
| Colour(1)(Gardner) | 8 |
| Viscosity(2)@ 77 °F | 680 |
| Viscosity(2)@ 50 °F | 5,000 |
| Amine Value(3), [mg KOH/g] | 350 |
| Specific Gravity(4) @ 77 °F | 0.993 |
| Flash Point(5) (closed cup) (°F) | 267 |
| Equivalent Wt/{H} | 93 |
| Recommended Use Level (phr, EEW=190) | 49 |
| TYPICAL HANDLING PROPERTIES | |
| Mixed Viscosity(6) @ 25 °C (cP) | 6640 |
| Gel Time(7) (150g mix @ 25 °C) (min) | 120 |
| Thin Film Set Time(8) @ 25 °C (hr) | 8 |
| Peak Exotherm(9) (100 g mass) (°C) | 65 |
| TYPICAL PERFORMANCE* | ||
| A* | B* | |
| Mixed Viscosity(2) @ 77 °F (cP) | 3,700 | 3,700 |
| Gel Time(6) (min) (150 g mix @ 77 °F) | 102 | 145 |
| Gel Time(6)(min) (150 g mix @ 50 °F) | 137 | 245 |
Thin Film Set Time(7) (hr) @ 77 °F | 8.5 | 12 |
| Thin Film Set Time(7) (hr) @ 50 °F | 14 | 35 |
| Thin Film Set Time(7) (hr) @ 40 °F | 28 | 35 |
| Peak Exotherm(8) (150 g mix @ 77 °F) (°F) | 178 | 116 |
| TYPICAL PERFORMANCE | ||
| (7 day cure @ 77 °F) | A* | B* |
| Glass Transition Temp(9)(°F) | 137 | 137 |
| Compressive Strength(10) @ yield (psi) | 13,600 | 10,900 |
| Compressive Modulus(10) (thousand psi) | 345 | 279 |
| Tensile Strength(11) (psi) | 8,600 | 8,700 |
| Tensile Modulus(11) ( thousand psi) | 243 | 190 |
| Tensile Elongation(11)@break(%) | 4.3 | 8.6 |
| Flexural Strength(12)(psi) | 17,300 | 13,600 |
| Flexural Modulus(12)(thousand psi) | 496 | 389 |
| Hardness(13) (Shore D) | 82 | 81 |
A* Ancamide 2396 formulated with DGEBA (EEW=190) resin
B* Ancamide 2396 with 90% DGEBA resin (EEW=190) and 10% Epodil® 748 diluent (C12−C14 alkyl glycidyl ether) blend
Note: Please see last page for footnotes.